Pureflon FKM
Description PureflonTM FKM Terpolymer Precompound is cured with bisphenol vulcanization system, which possess excellent fuel resistance, heat resistance, solvent resistance and bonding properties. It is an ideal material for fuel hoses, oil seals and gaskets, suitable for various processing methods.
Main Technical Properties
|
FKM Grade |
FKM Fluorine Content
(%) |
FKM Mooney Viscosity
ML(1+101 21℃) |
FKM Hardness
(Shore A) |
FKM Compression Set
200℃×70H (%) |
FKM TR10
(℃) |
|
BP301 |
68 |
30 |
76 |
22 |
-17 |
|
Low Mooney viscosity and excellent fluidity, suitable for injection and extrusion process. |
|
|
|
BP310T |
66 |
32 |
79 |
18 |
-18.8 |
|
Low Mooney viscosity and excellent low temperature resistance, suitable for injection and extrusion process. |
|
|
|
BP401 |
65.5 |
40 |
75 |
24 |
-19 |
|
Good fluidity and excellent low temperature resistance, suitable for injection, extrusion and molding process. |
|
|
|
BP501 |
68 |
50 |
77 |
20 |
-15 |
|
Excellent fluidity and low compression set, suitable for injection and molding process. |
|
|
|
BP561 |
68 |
50 |
76 |
24 |
-15 |
|
Excellent bonding properties and high elongation, suitable for injection and molding process. |
|
|
|
BP661 |
68 |
60 |
76 |
22 |
-15 |
|
Excellent bonding properties and adhesive properties, suitable for injection and molding process. |
|
|
|
BP701 |
68 |
70 |
77 |
20 |
-15 |
|
Excellent bonding property and high elongation, suitable for molding process. |
|
|
|
BP301G |
69.5 |
30 |
79 |
30 |
-8 |
|
High fluorine content and low Mooney viscosity, suitable for extrusion and molding process. |
|
|
|
BP361G |
69.5 |
30 |
79 |
30 |
-8 |
|
High fluorine content and excellent bonding properties, suitable for extrusion and molding process. |
|
|
|
BP501G |
69.7 |
48 |
79 |
31 |
-8 |
|
High fluorine content and middle Mooney viscosity, suitable for extrusion and molding process. |
Key Words: FKM Precompound, Compound FKM, Copolymer Precompound, Terpolymer Precompound |